High-temperature flexural strength of I-CVI processed Cf/SiC composites with variable interphases.

Singh, S and Singh, V and Kumari, S and Udayakumar, A and Bhanu Prasad, V.V (2021) High-temperature flexural strength of I-CVI processed Cf/SiC composites with variable interphases. Journal of the European Ceramic Society, 41 (1). pp. 130-135. ISSN 09552219

[img] Text
1-s2.0-S0955221920307160-main.pdf
Restricted to Registered users only

Download (4MB)
Official URL: https://www.sciencedirect.com/science/article/pii/...

Abstract

The effect of single-layer pyrocarbon (PyC) and multilayered (PyC/SiC)n=4 interphases on the flexural strength of un-coated and SiC seal-coated stitched 2D carbon fiber reinforced silicon carbide (Cf/SiC) composites was investigated. The composites were prepared by I-CVI process. Flexural strength of the composites was measured at 1200 °C in air atmosphere. It was observed that irrespective of the type of interphase, the seal coated samples showed a higher value of flexural strength as compared to the uncoated samples. The flexural strength of 470 ± 12 MPa was observed for the seal coated Cf/SiC composite samples with multilayered interphase. The seal coated samples with single layer PyC interphase showed flexural strength of 370 ± 20 MPa. The fractured surfaces of tested samples were analyzed in detail to study the fracture phenomena. Based on microstructure-property relations, a mechanism has been proposed for the increase of flexural properties of Cf/SiC composites having multilayered interphase.

Item Type: Article
Uncontrolled Keywords: Composites, SiC, Electron microscopy, Interphase
Subjects: CHEMISTRY AND MATERIALS > Composite Materials