Effect of PostNitride Annealing on Wear and Corrosion Behavior of Titanium Alloy Ti-6Al-4V

Anandan, C and Mohan, L (2016) Effect of PostNitride Annealing on Wear and Corrosion Behavior of Titanium Alloy Ti-6Al-4V. Journal of Materials Engineering and Performance, 25 (10). pp. 4416-4424. ISSN 10599495

[img] Text
Anandan-Mohan2016_Article_EffectOfPostNitrideAnnealingOn.pdf
Restricted to Registered users only

Download (2MB)
Official URL: https://link.springer.com/content/pdf/10.1007%2Fs1...

Abstract

Titanium alloy, Ti-6Al-4V, was plasma nitrided using RF plasma with 100% N at 800 °C and annealed at 850 °C in vacuum. XRD and XPS studies show the formation of titanium nitrides after nitriding and redistribution of nitrogen after annealing. Potentiodynamic polarization and electrochemical impedance spectroscopy studies in Hank’s solution show that nitriding decreases the corrosion resistance of the substrate and postnitride annealing improves the corrosion resistance of the nitrided samples. After nitriding, wear rate has decreased by an order of magnitude in reciprocating wear experiments and decreased further in annealed samples in comparison with that of substrate. Thus, postnitride annealing improves both corrosion and wear resistance of the nitrided sample. These improvements are attributed to redistribution of nitrogen and formation of a thin oxide layer on the sample due to annealing.

Item Type: Article
Subjects: CHEMISTRY AND MATERIALS > Chemistry and Materials (General)
CHEMISTRY AND MATERIALS > Composite Materials
Depositing User: Mrs SK Pratibha
Date Deposited: 18 Feb 2019 08:38
Last Modified: 18 Feb 2019 08:38
URI: http://nal-ir.nal.res.in/id/eprint/13075

Actions (login required)

View Item View Item