Fatigue life of a carbon fiber composite T-joint under a standard fighter aircraft spectrum load sequence

Thawre, MM and Pandey, KN and Dubey, A and Verma, KK and Peshwe, DR and Paretkar, RK and Jagannathan, N and Manjunatha, CM (2015) Fatigue life of a carbon fiber composite T-joint under a standard fighter aircraft spectrum load sequence. Composite Structures, 127. pp. 260-266. ISSN 02638223

Text 1-s2.0-S0263822315001981-main.pdf Restricted to Registered users only Download (1MB) | Request a copy

Abstract

The carbon fiber/epoxy composite (CFC) T-joints were fabricated and tested to determine their fatigue life under a standard fighter aircraft spectrum load sequence, mini-FALSTAFF with various reference loads. Further, the fatigue life of T-joint subjected to the same spectrum load sequence was predicted. For this purpose, the static pull-out (tension) and push-in (compression) tests were conducted on T-joints. Then, the constant amplitude fatigue tests were conducted to determine the load-life (P–N) curves at three different load ratio, R = Pmin/Pmax of 0.1, −1.0 and 10.0.The static and fatigue test data generated was then employed to construct constant life diagram (CLD) for T-joint. The fatigue damage for each of the rain flow counted load cycle of mini-FALSTAFF spectrum load sequence was determined using CLD. Using linear damage accumulation theory, the fatigue life of T-joint was estimated. The predicted fatigue life was observed to agree quite well with experimental results.

Item Type:	Article
Subjects:	AERONAUTICS > Aeronautics (General) CHEMISTRY AND MATERIALS > Composite Materials
Depositing User:	Mrs SK Pratibha
Date Deposited:	20 Jun 2018 10:28
Last Modified:	20 Jun 2018 10:28
URI:	http://nal-ir.nal.res.in/id/eprint/12838

Actions (login required)

View Item