High temperature deformation behavior of As-Cast Al-3Mg-).25Sc alloy

Suresh Kumar, M and Ambresha, M and Venkateswarlu, K and Ranganath, VR (2014) High temperature deformation behavior of As-Cast Al-3Mg-).25Sc alloy. Metallurgical and Materials Transactions A. xxx-1. ISSN 1073-5623

[img] PDF
meta_trans-final1.pdf - Accepted Version

Download (823kB)
Official URL: http://dx.doi.org/10.1007/s11661-014-2276-3

Abstract

High temperature deformation behavior of as-cast Al- 3Mg-0.25Sc alloy was characterized in a wide range of temperatures 573 K to 773 K (300 �C to 500 �C) and strain rates (0.001 to 10 s�1). A threshold stress behavior is observed in the temperature range of 573 K to 673 K (300 �C to 400 �C) due to interaction of dislocations with precipitates. In the temperature range of 573 K to 623 K (300 �C to 350 �C), the dislocations are pinned by precipitates, following Orowan-bowing mechanism. At 673 K (400 �C), the dislocations bypass the particles by climb process. At high temperature and low strain rate of 723 K (450 �C), and 0.001 s�1, respectively, the alloy exhibited high efficiency of power dissipation for opti- 22 mal hot working process.

Item Type: Article
Additional Information: Copyright to this article belongs to M/s. Springer, Boston
Uncontrolled Keywords: Al-Mg-Sc alloys;Superplastic materials;Computer-controlled servo-hydraulic machine
Subjects: AERONAUTICS > Aeronautics (General)
CHEMISTRY AND MATERIALS > Chemistry and Materials (General)
Depositing User: Ms. Alphones Mary
Date Deposited: 18 Jun 2014 04:31
Last Modified: 02 Nov 2015 03:23
URI: http://nal-ir.nal.res.in/id/eprint/11983

Actions (login required)

View Item View Item