Manohar , HR and Chandrashekharaiah, TM and Venkateswarlu, K and Kori, SA (2012) Dry sliding wear response of A413 alloy:Influence of intermetallics and test parameters. Tribology International, 51. pp. 54-60. ISSN 0301-679X
![]() |
PDF
tri_int_manohar.pdf Restricted to Registered users only Download (1MB) | Request a copy |
Abstract
Intermetallic particles of Al3Ti, TiB2, AlB2 and Al4Sr were added to A413 alloy, and sliding wear tests were carried out under dry sliding conditions at room temperature as well as at high temperatures of 60, 120,and180 1C. The results demonstrate that contacting surfaces at high temperature conditions are susceptible to oxidation and the wear rate of reinforced alloys is reduced. This is due to the formation of glazing layer that offers protection. Moreover,intermetallic particles played an important role as grain modifier/refiner and were responsible for reduced wear and friction.
Item Type: | Article |
---|---|
Additional Information: | Copyright for this article belongs to M/s. Elsevier BV |
Uncontrolled Keywords: | Aluminium–Silicon (A413);Intermetallic particle;Cylinder liners |
Subjects: | CHEMISTRY AND MATERIALS > Chemistry and Materials (General) CHEMISTRY AND MATERIALS > Composite Materials |
Depositing User: | Ms. Alphones Mary |
Date Deposited: | 07 Mar 2013 05:53 |
Last Modified: | 07 Mar 2013 05:53 |
URI: | http://nal-ir.nal.res.in/id/eprint/11501 |
Actions (login required)
![]() |
View Item |