Structure, optical properties and thermal stability of pulsed sputter deposited high temperature HfOx/Mo/HfO2 solar selective absorbers

Selvakumar, N and Barshilia, Harish C and Rajam, KS (2010) Structure, optical properties and thermal stability of pulsed sputter deposited high temperature HfOx/Mo/HfO2 solar selective absorbers. Solar Energy Materials and Solar Cells, 94 (8). pp. 1412-1420.

Full text available as:
[img] PDF (Journal) - Draft Version
Download (364Kb)

    Abstract

    Solar selective coatings of HfOx/Mo/HfO2 were deposited on copper (Cu) and stainless steel (SS) substrates using a magnetron sputtering system. The HfOx and HfO2 layers were deposited from the sputtering of Hf target in Ar+O2 plasma using an asymmetric bipolar-pulsed direct current generator. Whereas, the Mo layer was deposited from the sputtering of Mo target in the Ar plasma. The optimized HfOx/Mo/HfO2 multilayer absorber on Cu substrate exhibited high solar absorptance ( = 0.905-0.923) and low thermal emittance (82C = 0.07-0.09). Similarly, on SS substrates the optimized coatings exhibited  and 82C in the ranges of 0.902-0.917 and 0.15-0.17, respectively. The X-ray diffraction data showed that the HfOx/Mo/HfO2 coating consists of tetragonal and monoclinic phases of HfO2, which was confirmed by micro-Raman spectroscopy data. The bonding structure of the HfOx and the HfO2 layers were confirmed using X-ray photoelectron spectroscopy data. The optical constants (n and k), measured using spectroscopic ellipsometry, showed that the top HfO2 layer acts as an antireflection coating and the bottom two layers (HfOx and Mo) are the main absorber layers. The analysis of the spectroscopic ellipsometric data indicated that the band gap of the HfOx and the HfO2 layers were 3.90 and 5.82 eV, respectively, indicating non-stoichiometric nature of HfOx. In order to study the thermal stability of the HfOx/Mo/HfO2 coatings, they were subjected to heat treatment in air and vacuum at different temperatures (TA). The HfOx/Mo/HfO2 coatings deposited on Cu substrates were thermally stable up to 400°C for 2 hrs in air. Addition of a thin Mo interlayer (40 nm) in the HfOx/Mo/HfO2 coating (i.e., Mo/HfOx/Mo/HfO2) deposited on Cu substrates exhibited high solar selectivity (/) of 0.872/0.09 even after heat-treatment in air up to 500°C for 2 hrs. At TA = 525°C, the solar selectivity decreased drastically (/ = 0.761/0.35) due to the formation of MoO2, MoO3 and HfMo2O8 phases. The Mo/HfOx/Mo/HfO2 coatings deposited on SS substrates showed no significant changes in  and  values after annealing at 500°C in air and at 800°C in vacuum. These results were confirmed by micro-Raman spectroscopy measurements, which showed the compositional stability of these coatings up to 500°C in air and 800°C in vacuum.

    Item Type: Journal Article
    Subjects: RENEWABLE ENERGY > Solar Energy
    PHYSICS > Optics
    Division/Department: Surface Engineering Division, Surface Engineering Division, Surface Engineering Division
    Depositing User: Mr N Selvakumar
    Date Deposited: 26 Jul 2011 10:45
    Last Modified: 25 Aug 2011 10:21
    URI: http://nal-ir.nal.res.in/id/eprint/9640

    Actions (login required)

    View Item