Analysis of Failed Redler Link

Venkataswamy, MA and Parameswara, MA and Sujata, M and Bhaumik, SK (2004) Analysis of Failed Redler Link. Project Report. National Aerospace Laboratories, Bangalore.

Full text not available from this repository. (Request a copy)

Abstract

The redler link in question has failed during bend test due to presence of a surface defect. Investigation showed that the defect was a lap or fold that got created during forging. This had resulted in a discontinuity in the material with a sharp root. Subsequent carburising treatment had worsened the situation resulting in a highly sensitive notch in the component surrounded by a brittle material like carburising layer. Subsequent examination confirmed that the forging defects were present in the raw material (billet) itself and got translated into the defects seen in the final products. A detailed analysis of the problem is presented in this report and the recommendations are made to prevent recurrence of similar failures.

Item Type: Proj.Doc/Technical Report (Project Report)
Uncontrolled Keywords: Redler link;failure;forging defects;laps;folds
Subjects: AERONAUTICS > Aeronautics (General)
CHEMISTRY AND MATERIALS > Chemistry and Materials (General)
Division/Department: Materials Science Division, Materials Science Division, Materials Science Division, Materials Science Division
Depositing User: Mrs Manoranjitha M D
Date Deposited: 25 Jul 2011 10:13
Last Modified: 25 Jul 2011 10:13
URI: http://nal-ir.nal.res.in/id/eprint/9568

Actions (login required)

View Item